Апстракт:
Introduction : The degree of conversion of dental resin cement materials during polymerization process is very important for the longevity and quality of the clinical success of the restorative procedure. Insufficiently effective polymerization reaction of dental resin cement materials may result in adverse effects on the mechanical and adhesive performance of the material. It is believed that the proportion of triethylene glycol dimethacrylate (TEGDMA) monomers in the chemical structure of the material significantly influences the polymerization reaction. With the increase in TEGDMA, the degree of conversion of monomers into the polymer increases. Aim : The aim of this study was to determine the degree of polymerization of dual cure dental resin cement. Material and methods : For the analysis of the degree of polymerization Fourier transform infrared (FTIR) spectroscopy was used. 10 samples of dual cure resin based cement Variolink II were prepared in accordance with the manufacturer's instructions. Analysis was performed 24 hours after polymerization procedure. Results : Degree of polymerization of Variolink II resin based cement ranged from 69.2% to 98.7% with a mean value of 85.81%. Conclusion : Variolink II dual cure resin cement contains a significant percentage of TEGDMA which can be cause of high degree of polymerization. The minimum acceptable percentage of the degree of polymerization of dental resin cement has not yet been established.

Кључне речи:
dental resin cement,dual cure resin based cement,degree of polymerization,FTIR